High Impact Gloss Polystyrene Stress Crack Resistant - P91S Print
Issue A, 03-05
P91S - High Impact Gloss Polystyrene - Stress Crack Resistant
Standard Limitations
Unit
From
To
Sheet Thickness
mm
0.5
6.0
Sheet Width
mm
350
1520
Reel Thickness
mm
0.5
2.5
Reel Width
mm
350
800
Reel Diameter
mm
300
1000
Reel Weight
mm
50
300

Notes:
1) 0.5mm - 0.95mm sheet, maximum width 800mm
2) > 6.0mm - 8.0mm, MOQ 3 tonnes
3) > 1520mm - 2000mm, production campaign

For requirements outside these limits please contact your local AEL sales office.


Product Data Information
Applications Sanitary Ware, Refridgeration , Point Of Sale & Display, Insert Packaging.
Property                    
Test Method
Units
Base
Capping
Tensile Strength at Yield
ISO 527
MPa
25
50
Flexural Strength
ISO 178
MPa
40
90
Izod Impact Strength (notched) 23ºC
ISO 180
J/m
100
 
Heat Deflection Temperature (1.8 MPa)
ISO 75
ºC
82
81
Vicat Softening Point (5kg - 50ºC/h)
ISO 306
ºC
91
88
Density (1)
ISO 1183
 
1.05
1.05
Flammability Rating @ 1.5 mm
UL94
Class
HB
HB
Optical
Gloss

The above information represents typical property values that are based on information supplied by polymer raw material suppliers.
(1) Density value for natural unpigmented sheet - this value can change, the magnitude of such depending on the pigment type and loading.

Note:
We reserve the right to make alterations without further notice. Information in this data sheet is intended as a guide only. No liability is accepted for loss or damage arising from use or reliance on this information, or if such infringes any patent.


Ireland: Grace Rd, Athlone, Co Westmeath. Tel: +353 - 9064 - 92679. Fax: +353 - 9064 - 94086
UK: Equipoint, Coventry Road, Birmingham B25 8AD. Tel: +44 - 121 - 764 4848. Fax +44 - 121 - 764 4443
Netherlands: Schouwburgring 85, 5038 TK Tilburg, The Netherlands. Tel: +31 - 13 - 544 7265. Fax: +31 - 13 - 544 2747